ASME SA333/SA333M GR6 Seamless Steel Pipe ASTM A333 Gr6 Low Temperature Steel Pipes

A333 PIPE SPECIFICATIONS

NPS 1/4″ – 42″

Schedules 10 through 160, STD, XH and XXH

Scope

ASTM A333 covers nominal (average) wall seamless and welded carbon and alloy steel pipe intended for use at low temperatures. Several grades of ferritic steel are included. Some product sizes may not be available under this specification because heavier wall thicknesses have an adverse affect on low-temperature impact properties.
Looking for specific post-production services? See our full list.

Material & Manufacture

The pipe shall be made by the seamless or welding process with the addition of no filler metal in the welding operation.

Heat Treatment Requirements

All seamless and welded pipe shall be treated to control their microstructure by the following methods: Normalizing per A 333/A 333M-05 section 4.3.1.1; section 4.3.1.2 or section 4.3.1.3 Quenched and Tempered per A 333/A 333M – 05 section 4.3.2.1 Double Normalized and Tempered per A 333/A 333M – 05 section 4.3.2.2

Chemical Requirements

For each reduction of 0.01% carbon below 0.30%, an increase of 0.05% manganese above 1.06% would be permitted to a maximum of 1.35% manganese. When Grade 6 is ordered under this specification, supplying an alloy grade that specifically requires the addition of any element other than those listed for the ordered grade is not permitted. However, the addition of elements required for the deoxidation of the steel is permitted.
Download the full product catalog.

Tensile Requirements

The material shall conform to the requirements as proscribed:

Impact Requirements

For Grades 1, 3 and 6, the notched-bar impact properties of each set of three impact specimens, including specimens for the welded joint in welded pipe with wall thicknesses of 0.120 in. [3 mm] and larger, shall not be less than the values prescribed:

Mechanical Testing

Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested. For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe. Hydrostatic Test Impact Test One notched bar impact test, consisting of breaking three specimens shall be made from each heat represented in a heat-treatment load on specimens taken from the finished pipe.